Hempel Tiger Xtra Antifoul 2.5L

iger Xtra is a self polishing, erodible antifouling. Suitable to both power and sail boats and just 1 coat can last the season. Applying a second coat for year round protection gives excellent and consistent long term performance, under all conditions. It is suitable for use on all substrates except aluminium.

Features
- High mechanical strength for excellent crack resistance
- Suitable for dry sailing or continuous immersion.

Application
Thinner
Hempel's Thinner 08080
Cleaner
Hempel's Thinner 08080
Hempel's Thinner 808 08081

Application method Tool Thinning Max Vol.
Brush/Roller 5%
Paint Pad 5%

If the vessel is regularly used at speeds above 20 knots, it is recommended to
apply 3 coats of antifouling. The product can be applied by spray. Contact
Hempel for more information. Keep thinning at an absolute minimum.
Film thickness

Theoretical spreading rate 13 m²/L [530 sq ft/US gal]

Application conditions
- To avoid condensation, apply on a clean and dry surface with a
temperature that is at least 3°C [5°F] above the dew point.

Relative Humidity:
- Relative humidity must be below 85% during application.

Application remarks
- Copper containing antifouling must not have any electrical contact
with aluminium hull and other aluminium components.
- Apply 2 coats of the Antifouling paint at 40 μm dry film thickness
each. Apply an additional coat around the waterline and high wear
areas. Wear protective gloves/clothing and eye/face protection.
- Stir well before use.

Drying and overcoating
Product compatibility
- Previous coat: Recommended products are: Hempel's Light Primer,
Hempel's Underwater Primer, Hempel's Pro Tiecoat
Drying time
Touch dry 30 minutes 9 minutes depending on temperature.

Determined for dry film thickness 40 micron [1.6 mils] at standard conditions,
see Hempel’s Explanatory Notes for details. Time to immersion: Minimum: 24
Hours 20°C ; Maximum 6 months

Drying conditions
- To obtain the drying time stated, it is important to maintain sufficient
ventilation during application, drying and curing.
- Condensation on the freshly applied coating should be avoided.